Mesoscale simulation of the mold filling process of Sheet Molding Compound
Nils Meyer
2022
0 Ungluers have
Faved this Work
Login to Fave
Sheet Molding Compounds (SMC) are discontinuous fiber reinforced composites that are widely applied due to their ability to realize composite parts with long fibers at low cost. A novel Direct Bundle Simulation (DBS) method is proposed in this work to enable a direct simulation at component scale utilizing the observation that fiber bundles often remain in a bundled configuration during SMC compression molding.
This book is included in DOAB.
Why read this book? Have your say.
You must be logged in to comment.
Rights Information
Are you the author or publisher of this work? If so, you can claim it as yours by registering as an Unglue.it rights holder.Downloads
This work has been downloaded 29 times via unglue.it ebook links.
- 29 - pdf (CC BY-SA) at Unglue.it.
Keywords
- CoDiCoFRP
- compression molding
- Fließpressen
- Mechanical engineering & materials
- process simulation
- Prozesssimulation
- sheet molding compound
- Technology, engineering, agriculture
Links
DOI: 10.5445/KSP/1000143703Editions